Chen WC et al. - The results show that while composite, the hard–brittle properties of 25 wt% polyacrylic acid are proportional to CPC and mixing with additives is the same as those of the CPC without polyacrylic acid added. With an increase of polyacrylic acid/CPC ratio, the 67 wt% samples revealed ductile–tough properties and 100 wt% samples kept ductile or elastic properties after 24 h of immersion. The modulus range of this development was from 200 to 2600 MPa after getting immersed in simulated body fluid for 24 h.
|
 |
|