See Latest ArticlesEffect of sintering time on biaxial strength of zirconium dioxide
Dental Materials, 07/17/08
Hjerppe J et al. - No statistically significant difference (p > 0.05) was found between the groups in terms of sintering time or thermocycling. The biaxial flexural strength of the groups varied from 995 MPa to 1127 MPa. Surface microhardness varied from 1478 to 1532. The relative amount of the monoclinic phase was higher when zirconia was thermocycled and stored in water compared to control discs, which had no monoclinic phase at all.
Today in Dental Materials...keeping you current
Receive free subspecialty "5-minute updates" via email
Randomized Controlled Clinical Trial of Zirconia-Ceramic and Metal-Ceramic Posterior Fixed Dental Prostheses: A 3-year Follow-up
The International Journal of Prosthodontics, 11/19/09
Factors Affecting Survival and Usefulness of Implants Placed in Vascularized Free Composite Grafts Used in Post–Head and Neck Cancer Reconstruction
Clinical Implant Dentistry and Related Research, 10/28/09
Dental Enamel Irradiated with Infrared Diode Laser and Photo-Absorbing Cream
Photomedicine and Laser Surgery, 11/05/09
Today in Prosthodontics/Restore...keeping you current
Receive free subspecialty "5-minute updates" via email
The future of complete dentures in oral rehabilitation. A critical review
Journal of Oral Rehabilitation, 12/16/09
Recessive dystrophic epidermolysis bullosa—oral rehabilitation using stereolithography and immediate endosseous implants
Special Care in Dentistry, 12/15/09
Fabricating a Nonrotational Angulated Abutment for a Single-Tooth Prosthesis
Implant Dentistry, 12/15/09